*A Summary of Changes section appears at the end of this standard

of this test method. Nonstandard conditions and the reasons for
departure from standard conditions shall be reported clearly
and prominently with comparator values.
5. Apparatus
5.1 Molds and Length Comparator—The molds for casting
test specimens and the length comparator for measuring length
change shall conform to the requirements of Practice
C 490
.
5.2 Tamper—The tamper shall be made of a nonabsorptive,
nonabrasive material such as medium-hard rubber or seasoned
oak wood rendered nonabsorptive by immersion for 15 min in
paraffin at approximately 392 °F [200 °C], and shall have a
cross section of
1
⁄
2
by 1.0 in. [13 by 25 mm] and a convenient
length of about 6 in. [150 mm]. The tamping face of the tamper
shall be flat and at right angles to the length of the tamper.
5.3 Tamping Rod—The tamping rod shall be a straight steel
rod
3
⁄
8
in. [10 mm] in diameter and not less than 10 in. [250
mm] in length, having at least the tamping end rounded to a
hemispherical tip of the same diameter.
5.4 Drying Room and Controls—A drying room with suit-
able racks shall be provided when storing specimens in air. The
racks shall be designed for free circulation of air around
specimens, except for necessary supports, and shall be so
situated with respect to the nearest wall or other obstruction
that air circulation is not restricted in the intervening space.
The supports shall be horizontal and shall consist of two
nonabsorptive members not deeper than 1 in. [25 mm] and
having a bearing area of not more than
1
⁄
4
in. [6 mm] in width.
Conditioned air shall be circulated into and out of the room in
a uniform manner so that the specified rate of evaporation is
attained adjacent to all specimens.
5.4.1 The air in the room shall be maintained at a tempera-
ture of 73 6 3 °F [23 6 2 °C] and a relative humidity of 50 6
4 %. The air movement past all specimens shall be such that
the rate of evaporation is 77 6 30-mL/24 h from an atmometer
or 13 6 5-mL/24 h from a 400-mL Griffin low-form beaker
filled to
3
⁄
4
in. [20 mm] from the top. The temperature and
relative humidity of the air in the room shall be measured with
either a sling or Assmann psychrometer at least twice each
working day. The psychrometer shall comply with Test Method
E 337
, except that thermometers having an overall length of 10
in. [250 mm] and marked in subdivisions of 0.5 °F [0.25 °C]
are permitted. The room shall be equipped with a means of
measuring and recording wet- and dry-bulb temperatures
continuously. Correction factors as indicated by the sling or
Assmann psychrometer shall be applied to the recorded data.
The rate of evaporation within the room shall be determined
daily by the use of the atmometer or by the loss of mass of
water from a 400-mL Griffin low-form beaker filled initially to
3
⁄
4
in. [20 mm] from the top.
5.5 Atmometer—The atmometer shall be constructed as
shown in
Fig. 1
.
5.5.1 Mounting—
Fig. 2
shows a suggested arrangement for
operating the atmometer. Punch a central hole
1
⁄
2
in. [13 mm]
in diameter in a filter paper, place it on the atmometer, and
secure it in place while dry, by turning the torque handle only,
until it just starts to slip. Mount the atmometer on a stand with
the filter paper in a horizontal position. Mount a 100-mL glass
graduate so that the 100-mL mark is from 1 to 3 in. [25 to 75
mm] below the level of the filter paper. Stopper the graduate so
that entrance is provided for two short glass tubes not extend-
ing to the water level and one long tube extending to the
bottom of the graduate. Connect the glass tubing leading from
the bottom of the graduate to the inlet of the atmometer by
means of clear plastic tubing.
5.5.2 Operation—Use clear plastic tubing to connect a
squeeze bottle containing distilled or deionized water to one of
the short glass tubes into the graduate. Force water into the
graduate until it is about half full and then close the remaining
glass tube into the graduate. Continue to force water through
the graduate into the atmometer until the filter paper is
saturated and there are no air bubbles in the system. Open the
glass tube into the graduate and release pressure on the squeeze
bottle gradually to avoid trapping air in the tube leading to the
atmometer. Adjust the level of water in the graduate to
approximately the 100-mL mark. If the atmometer is to be used
under variable temperature conditions, disconnect the squeeze
bottle after filling the graduate to avoid the possibility of
additional water being forced into the graduate. Permit evapo-
ration of water from the filter paper for 1 h before recording the
time and initial reading of the graduate. It is not permitted to
omit the waiting period during subsequent use of the atmom-
eter provided the filter paper does not become dry. Change the
filter paper whenever it shows signs of contamination but not
less frequently than once every two weeks.
5.6 Filter Paper—The filter paper to be used with the
atmometer shall be white with a smooth surface texture. It shall
be 6 in. [152 mm] in diameter and 0.050 6 0.003 in. [1.27 6
0.08 mm] thick and shall have a cotton fiber content of not less
than 75 weight %. The density shall be between 0.400 and
0.425 g/cm
3
. The Mullen bursting strength shall not be less
than 50 psi [345 kPa].
N
OTE
1—E and D filter paper No. 625
3
has been found suitable.
5.7 Apparatus for Demolding Specimens—It is useful to
construct an apparatus for demolding specimens molded in
double molds as detailed in
Fig. 3
or to a different design that
serves the same purpose. When this device is to be used, the
center side plate of the double mold must be appropriately
drilled and tapped to receive the 8-32 by
5
⁄
8
in. [4.5-0.74 IMC
by 16 mm] machine screw of the demolding thumbscrew.
Fig.
4
shows the details of a suitable apparatus for demolding
specimens molded in single molds.
3
The sole source of supply of the apparatus known to the committee at this time
is Ahlstrom Filtration Co., Mt. Holly Springs, PA 17065. If you are aware of
alternative suppliers, please provide this information to ASTM International
Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee,
1
which you may attend.

tải về 128.58 Kb.

Chia sẻ với bạn bè của bạn: