Effect of Zn on dielectric properties of Mn-Zn spinel ferrite synthesized by coprecipitation

4. Conclusion 
In this study, Mn
1-x
Zn
x
Fe
2
O
4 
spinel ferrite was synthesized by coprecipitation method with synthesis temperature 
120°C. XRD result confirms cubic spinel structures. The particle sizes decrease by increasing Zn concentration. For 
zink rich, the dielectric parameter such as real dielectric constant, imaginary dielectric constant, loss tangent and AC 
conductivity decreases by increasing Zn concentrations. The dielectric constant exhibited decreasing trend with 
increasing frequency while loss tangent and AC conductivity increase by increasing frequency. 
Acknowledgements 
This research supported and funded by Indonesia endowment fund for education (LPDP) and Grant of “Penelitian 
Berbasis Kompetensi”, Ministry of Research, Technology and Higher Education of the Republic Indonesia 
(Kementerian Ristek Dikti) 2017 for financing this research. 
References 
[1] D.S Mathew, R.S. Juang, Chemical engineering journal, 129 (2007) 51-65. 
[2] M.R. Syue, F.J. Wei, C.S. Chou and C.M. Fu, Thin Solid Films, 519 (2011) 8303-8306. 
[3] U.R. Ghodake, R.C. Kambale and S.S. Suryavanshi, Ceramics International, 43(2017) 1129-1134. 
[4] V.D. Mote, Y. Purushotman and B.N. Dole, Material and Design, 96 (2016) 99-105. 
[5] K. Jalaiah, K. Vijaya Babu, Journal of Magnetism and Magnetic Materials, 423 (2017) 275-280. 
[6] I.P.T. Indrayana, N. Siregar, E. Suharyadi, T. Kato, S. Iwata, Journal of Physics: Conference Series 776 (2016) 012021. 
[7] S.H. Kareem, A.A. Ati, M. Shamsuddin and S.L. Lee, Ceramics International, 41 (2015) 11702-11709. 
[8] M. Hashim, Alimuddin, S. Kumar, B.H. Koo, S.E. Shirshath, E.M. Mohammed, J. Shah, R.K. Kotnala, H.K. Choi, H. Chung and R. Kumar, 
Journal of Alloys and Compounds, 518 (2012) 11-18. 
[9] V.J. Angadi, L. Choudhury, K. Sadhana, H.L.Liu, R. Sandhya, S. Matteppanavar, B. Rudraswamy, V. Pattar, R.V. Anavekar and K. Praveena, 
Journal of Magnetism and Magnetic Materials, 424 (2017) 1-11. 
[10] S.Atiq, M. Majeed, A. Ahmad, S.K. Abbas, M. Saleem and S. Riaz, Ceramics International, 43 (2017) 2486-2494. 
[11] Y. Koseoglu, Ceramics International, 39 (2013) 4221-4230.