Designation: c 157/C 157M – 08 Standard Test Method for Length Change of Hardened Hydraulic-Cement Mortar and Concrete 1

tải về 128.58 Kb.
Chế độ xem pdf
Chuyển đổi dữ liệu31.01.2024
Kích128.58 Kb.
1   2   3   4   5   6   7   8   9   10

C 157/C 157M – 08
Copyright by ASTM Int'l (all rights reserved); Thu Apr 16 06:09:51 EDT 2009
Downloaded/printed by
Laurentian University pursuant to License Agreement. No further reproductions authorized.

more closely controlled temperature as was done prior to the
earlier reading and in the manner described above.
3—To determine the drying shrinkage of concrete subjected to
elevated temperature curing in the laboratory, a modification of the
previous method is necessary. Where concrete is cured with elevated
(non-autoclave) temperatures, the curing cycle for this test method shall
be that to be used for the project structural members. The elevated
temperature curing cycle consists of pre-steam, steam cure, and post-
steam periods. To avoid measuring thermal volume change, after the
molds are stripped, cool drying-shrinkage specimens at laboratory tem-
perature until they reach equilibrium (approximately 6 h for 4 by 4 by
11-in. [100 by 100 by 280-mm] bars). Then place them in lime-saturated
water prior to the initial reading (see
11. Procedure for Storage of Specimens
11.1 After measurement at the end of the curing period,
store the specimens as described in either of the following:
11.1.1 Water Storage—Immerse the specimens in lime-
saturated water storage in accordance with Specification
C 511
Take comparator readings of each specimen when it has
reached an age, including the curing period of 8, 16, 32, and 64
weeks. Make these readings immediately after the specimens
have been subjected to storage in water at 73 6 1 °F [23 6 0.5
°C] for at least 15 min in the case of 1-in. [25-mm] specimens
or 30 min in the case of 3-in. [75-mm] or 4-in. [100-mm]
11.1.2 Air Storage—Store the specimens in the drying
room, so that the specimens have a clearance of at least 1 in. or
25 mm on all sides. Take comparator readings of each
specimen after periods of air storage after curing of 4, 7, 14,
and 28 days, and after 8, 16, 32, and 64 weeks. Preferably, take
these readings in a room maintained at a relative humidity of
50 6 4 % while the specimens are at a temperature of 73 6 3
°F [23 6 2 °C].