W8056HGB GLOSS (50%)PRODUCT INTRODUCTION Description Rapid Single Component Water-base Modified Polysiloxane Gloss Top-coat. Uses Furniture, Flooring and Paneling made from timber. Application Spray COATING PERFORMANCE
PHYSICAL AND CHEMICAL PROPERTIES Specific Gravity at 27 (oC) 1.00 – 1.06 (Clear) Solid Content (%) 28 – 32 (Clear) Viscosity ( at 27 oC ) 35 – 45 sec F #4 Cup Binder Type Modified Polysiloxane PRODUCT PREPARATION Mixing Ratio W8056HGB Gloss 100 parts by weight Reducer 0 to 50 parts by weight Reducer W8046R Reducer APPLICATION PARAMETER Theoretical Coverage (m2/L) 10 – 16 (subject to substrate porosity). Coating System 1 or 2 coats of sanding sealer (W8029 / W8348), sanded, followed by 2 to 3 coats of W8056 Gloss. Application temperature 10 oC - 50 oC Touch-dry Time (27 oC) 10 – 15 minutes Hard-dry Time (at 27oC) About 30 minutes. GENERAL PROPERTIES W8056HGB Gloss is a water-based rapid single component Modified Polysiloxane Top-coat formulated specially for application on timber substrate via spray application. This product is designed for self cross-linking to provide a rapid curing, hard and durable coating with excellent scrub, UV, stain, water, fungus and dirt pick-up resistance. This product is free of formaldehyde and being water-based, is non-flammable. W8056HGB Gloss is available in transparent water-clear, transparent stain as well as solid (opaque) colouration. SHELF LIFE 12 months from date of manufacture. The date refers to product held in its original closed packaging. STORAGE Keep containers in a cool ventilated environment, temperature between 5 oC to 40 oC. With partial use, close container tight and use the remainder as soon as possible. W8056HGB GLOSS (50%) Advance water-based wood lacquer FILM PROPERTIES
CONTROLLED MATERIALS IN WET PAINT
* These chemicals are not used in the manufacture of our product. However, minute traces may be present due to environmental contamination beyond our control. COMMENT Tests were performed on paint films applied at 100 wet film and allowed to cure at 27 2oC for 7 days. Relative Humidity was maintained at 80% during the period of film curing. 
The information in this brochure has been compiled in accordance to our best knowledge at the date of issue and is based on recent technological and scientific developments. However, this information should not be construed into recommending the use of our product in violation of any patent or as warranties (express or implied) of non-infringement or its fitness for any particular purpose. Prospective purchasers are invited to conduct their own tests and studies to determine the fitness Biochem products for their particular purposes and specific applications. Due to the varying techniques and conditions applied, Biochem accepts no responsibility for any use of the product, may be by way of experiment or manufacture nor does Biochem accepts any responsibility for the used techniques in any application whatsoever. Biochem does not warrant against infringement of patents of third parties by reason of any uses purchasers make of the product. *Biochem: Biochem International J.S. Company Каталог: tailieu -> tds anh tailieu -> A. ĐẠi số TỔ HỢp I. Kiến thức cơ bản quy tắc cộng tailieu -> Wikipedia luôn có mặt mỗi khi bạn cần giờ đây Wikipedia cần bạn giúp tailieu -> CHÍnh phủ CỘng hòa xã HỘi chủ nghĩa việt nam độc lập Tự do Hạnh phúc tailieu -> VĂn phòng cộng hoà XÃ HỘi chủ nghĩa việt nam tds anh -> 118 Nguyen Phi Khanh St, Tan Dinh Ward, District 1, Ho Chi Minh City, Vietnam tải về 28.46 Kb. Chia sẻ với bạn bè của bạn:
|